Electronic properties of phases in the quasi-binary Bi[sub]2Se[sub]3-Bi[sub]2S[sub]3 system
Zipporah Rini Benher, Sandra Gardonio, Mattia Fanetti, Paolo Moras, Asish K. Kundu, Chiara Bigi, Matjaž Valant, 2021, izvirni znanstveni članek

Opis: We explored the properties of the quasi-binary Bi2Se3–Bi2S3 system over a wide compositional range. X-ray diffraction analysis demonstrates that rhombohedral crystals can be synthesized within the solid solution interval 0–22 mol% Bi2S3, while at 33 mol% Bi2S3 only orthorhombic crystals are obtained. Core level photoemission spectroscopy reveals the presence of Bi3+, Se2− and S2− species and the absence of metallic species, thus indicating that S incorporation into Bi2Se3 proceeds prevalently through the substitution of Se with S. Spin- and angle-resolved photoemission spectroscopy shows that topological surface states develop on the surfaces of the Bi2Se3−ySy (y ≤0.66) rhombohedral crystals, in close analogy with the prototypical case of Bi2Se3, while the orthorhombic crystals with higher S content turn out to be trivial semiconductors. Our results connect unambiguously the phase diagram and electronic properties of the Bi2Se3–Bi2S3 system.
Najdeno v: osebi
Ključne besede: topological insulator, quasi-binary Bi2Se3-Bi2S3 system, electronic properties