21. SnO2-Containing Clinoptilolite as a Composite Photocatalyst for Dyes Removal fromWastewater under Solar LightAndraž Šuligoj, Jelena Pavlovič, Iztok Arčon, Nevenka Rajić, Nataša Novak Tušar, 2020, izvirni znanstveni članek Opis: Due to their adsorbent, ion exchange and catalytic properties zeolites are suitable for a variety of applications. We report on the photocatalytic activity of a readily available and inexpensive natural zeolite clinoptilolite (Z) containing SnO2 (Sn-Z). The Sn-Z samples with 3–15 wt. % of Sn were prepared by using a precipitation–deposition method. Powder X-ray diffraction analysis showed that the zeolite structure was unaffected by the introduction of the Sn-phase. Diffuse reflectance UV/VIS spectra of the Sn-Z samples confirmed the presence of SnO2 and X-Ray absorption spectroscopy analyses suggested that the SnO2 particles mainly resided on the surface of the clinoptilolite, while ATR-FTIR analysis gave some clues that part of the SnO2 phase was incorporated in the pores of the zeolite. The presence of SnO2 in Sn-Z increased both adsorption capacity and photocatalytic performance which could be partially explained by higher surface area and partially with an increased negative potential of the surface. Adsorption and total degradation of methylene blue (MB) for the Sn-Z with the highest amount of Sn (15 wt.%) was about 30% and 45%, respectively, suggesting a synergetic effect between SnO2 and the clinoptilolite lattice. Reusability tests showed that these catalysts present a promising material for water purification.
Najdeno v: osebi
Ključne besede: SnO2, zeolite, SnO2-clinoptilolite composite, photocatalysis, solar light, methylene blue
removal, wastewater treatment
Objavljeno: 25.02.2020; Ogledov: 1784; Prenosov: 93
 Polno besedilo (3,50 MB) |
22. Insight into the interdependence of Ni and Al in bifunctional Ni/ZSM-5 catalysts at the nanoscaleNataša Novak Tušar, Nataša Zabukovec Logar, Gregor Mali, Janez Volavšek, Simone Pollastri, Goran Dražić, Danilo Oliveira de Souza, Iztok Arčon, Hue-Tong Vu, 2022, izvirni znanstveni članek Opis: Catalyst design is crucial for improving catalytic activity and product selectivity. In a bifunctional Ni/ZSM-5
zeolite type catalyst, catalytic properties are usually tuned via varying Al and Ni contents. While changes in
acid properties associated with Al sites are usually closely investigated, Ni phases, however, receive
inadequate attention. Herein, we present a systematic structural study of Ni in the Ni/ZSM-5 materials by
using Ni K-edge XANES and EXAFS analyses, complemented by XRD and TEM, to resolve the changes in
the local environment of Ni species induced by the different Al contents of the parent ZSM-5 prepared
by a “green”, template free technique. Ni species in Ni/ZSM-5 exist as NiO crystals (3–50 nm) and as
charge compensating Ni2+ cations. The Ni K-edge XANES and EXAFS results enabled the quantification
of Ni-containing species. At a low Al to Si ratio (nAl/nSi # 0.04), the NiO nanoparticles predominate in
the samples and account for over 65% of Ni phases. However, NiO is outnumbered by Ni2+ cations
attached to the zeolite framework in ZSM-5 with a high Al to Si ratio (nAl/nSi ¼ 0.05) due to a higher
number of framework negative charges imparted by Al. The obtained results show that the number of
highly reducible and active NiO crystals is strongly correlated with the framework Al sites present in
ZSM-5 zeolites, which depend greatly on the synthesis conditions. Therefore, this kind of study is
beneficial for any further investigation of the catalytic activities of Ni/ZSM-5 and other metal-modified
bifunctional catalysts.
Najdeno v: osebi
Ključne besede: Ni/ZSM-5 catalysts, zeolite, Ni XANES, EXAFS
Objavljeno: 11.05.2022; Ogledov: 246; Prenosov: 7
Polno besedilo (1,25 MB)
Gradivo ima več datotek! Več...
|