Naslov:Photo-Chemically-Deposited and Industrial Cu/ZnO/Al2O3 Catalyst Material Surface Structures During CO2 Hydrogenation to Methanol: EXAFS, XANES and XPS Analyses of Phases After Oxidation, Reduction, and Reaction
Avtorji:ID Pori, Maja, Uni-Lj (Avtor)
ID Arčon, Iztok, UNG (Avtor)
ID Dasireddy, Venkata, Uni-Kwazului (Avtor)
ID Likozar, Blaž, KI (Avtor)
Datoteke: Gradivo nima datotek, ki so prostodostopne za javnost. Gradivo je morda fizično dosegljivo v knjižnici fakultete, zalogo lahko preverite v COBISS-u. Povezava se odpre v novem oknu
Jezik:Angleški jezik
Vrsta gradiva:Delo ni kategorizirano
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:UNG - Univerza v Novi Gorici
Opis:Industrial Cu/ZnO/Al2O3 or novel rate catalysts, prepared with a photochemical deposition method, were studied under functional CH3OH synthesis conditions at the set temperature (T) range of 240–350 °C, 20 bar pressure, and stoichiometric carbon dioxide/hydrogen composition. Analytical scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), X-ray adsorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) methods were systematically utilized to investigate the interfaces, measured local geometry, and chemical state electronics around the structured active sites of commercially available Cu/ZnO/Al2O3 material or synthesized Cu/ZnO. Processed Cu K-edge EXAFS analysis suggested that various Cu atom species, clusters, metallic fcc Cu, Cu oxides (Cu2O or CuO) and the Cu0.7Zn2 alloy with hexagonal crystalline particles are contained after testing. It was proposed that in addition to the model’s Cu surface area, the amount, ratio and dispersion of the mentioned bonded Cu compounds significantly influenced activity. Additionally, XPS revealed that carbon may be deposited on the commercial Cu/ZnO/Al2O3, forming the inactive carbide coating with Cu or/and Zn, which may be the cause of basicity’s severe deactivation during reactions. The selectivity to methanol decreased with increasing T, whereas more Cu0.7Zn2 inhibited the CO formation through reverse water–gas shift (RWGS) CO2 reduction.
Ključne besede:CH3OH synthesis, Cu/ZnO-based catalyst, XPS, XANES, EXAFS analyses, Catalyst selectivity and activity
Verzija publikacije:Preprint, delovna različica publikacije (nerecenzirana)
Leto izida:2021
Št. strani:10
Številčenje:1
PID:20.500.12556/RUNG-6568 Novo okno
COBISS.SI-ID:65711875 Novo okno
DOI:10.1007/s10562-021-03556-1 Novo okno
NUK URN:URN:SI:UNG:REP:IKEEQI88
Datum objave v RUNG:03.06.2021
Število ogledov:3778
Število prenosov:0
Metapodatki:XML DC-XML DC-RDF
:
PORI, Maja, ARČON, Iztok, DASIREDDY, Venkata in LIKOZAR, Blaž, 2021, Photo-Chemically-Deposited and Industrial Cu/ZnO/Al2O3 Catalyst Material Surface Structures During CO2 Hydrogenation to Methanol: EXAFS, XANES and XPS Analyses of Phases After Oxidation, Reduction, and Reaction. Catalysis Letters [na spletu]. 2021. Vol. 1. [Dostopano 7 april 2025]. DOI 10.1007/s10562-021-03556-1. Pridobljeno s: https://repozitorij.ung.si/IzpisGradiva.php?lang=slv&id=6568
Kopiraj citat
  
Skupna ocena:
0.5
1
1.5
2
2.5
3
3.5
4
4.5
5
(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
Objavi na:Bookmark and Share


Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše podrobnosti ali sproži prenos.

Gradivo je del revije

Naslov:Catalysis Letters
Leto izida:2021

Nazaj