Photo-Chemically-Deposited and Industrial Cu/ZnO/Al2O3 Catalyst Material Surface Structures During CO2 Hydrogenation to Methanol: EXAFS, XANES and XPS Analyses of Phases After Oxidation, Reduction, and Reaction
Blaž Likozar, Iztok Arčon, Venkata Dasireddy, Maja Pori, 2021, original scientific article

Abstract: Industrial Cu/ZnO/Al2O3 or novel rate catalysts, prepared with a photochemical deposition method, were studied under functional CH3OH synthesis conditions at the set temperature (T) range of 240–350 °C, 20 bar pressure, and stoichiometric carbon dioxide/hydrogen composition. Analytical scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), X-ray adsorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) methods were systematically utilized to investigate the interfaces, measured local geometry, and chemical state electronics around the structured active sites of commercially available Cu/ZnO/Al2O3 material or synthesized Cu/ZnO. Processed Cu K-edge EXAFS analysis suggested that various Cu atom species, clusters, metallic fcc Cu, Cu oxides (Cu2O or CuO) and the Cu0.7Zn2 alloy with hexagonal crystalline particles are contained after testing. It was proposed that in addition to the model’s Cu surface area, the amount, ratio and dispersion of the mentioned bonded Cu compounds significantly influenced activity. Additionally, XPS revealed that carbon may be deposited on the commercial Cu/ZnO/Al2O3, forming the inactive carbide coating with Cu or/and Zn, which may be the cause of basicity’s severe deactivation during reactions. The selectivity to methanol decreased with increasing T, whereas more Cu0.7Zn2 inhibited the CO formation through reverse water–gas shift (RWGS) CO2 reduction.
Found in: ključnih besedah
Summary of found: ...the mentioned bonded Cu compounds significantly influenced activity. Additionally, XPS revealed that carbon may be...
Keywords: CH3OH synthesis, Cu/ZnO-based catalyst, XPS, XANES, EXAFS analyses, Catalyst selectivity and activity
Published: 03.06.2021; Views: 339; Downloads: 0
.pdf Fulltext (3,98 MB)

Improved photocatalytic activity of SnO[sub]2-TiO[sub]2 nanocomposite thin films prepared by low-temperature sol-gel method
Urška Lavrenčič Štangar, Giovanni Palmisano, Matjaž Valant, Mattia Fanetti, Samar Al Jitan, Iztok Arčon, Ksenija Maver, 2021, original scientific article

Abstract: The objective of this research was to investigate how the photocatalytic activity of pure TiO2 can be improved by SnO2 modification. Different molar ratios of tin to titanium were prepared. The correlation between tin concentration and structural properties was investigated to explain the mechanism of photocatalytic efficiency and to optimize the synthesis conditions to obtain enhanced activity of the SnO2-modified TiO2 photocatalysts under UV-irradiation. The SnO2-modified TiO2 photocatalysts were prepared by a low-temperature sol-gel method based on organic tin and titanium precursors. The precursors underwent sol-gel reactions separately to form SnO2-TiO2 sol. The sol-gels were deposited on a glass substrate by a dip-coating technique and dried at 150 ◦C to obtain the photocatalysts in the form of a thin film. To test the thermal stability of the material, an additional set of photocatalysts was prepared by calcining the dried samples in air at 500 ◦C. The photocatalytic activity of the samples was determined by measuring the degradation rate of an azo dye. An increase of up to 30% in the photocatalytic activity of the air-dried samples was obtained when the TiO2 was modified with the SnO2 in a concentration range of 0.1–1 mol.%. At higher SnO2 loadings, the photocatalytic activity of the photocatalyst was reduced compared to the unmodified TiO2. The calcined samples showed an overall reduced photocatalytic activity compared to the air-dried samples. Various characterization techniques (UV-Vis, XRD, N2-physisorption, TEM, EDX, SEM, XAS and photoelectrochemical characterization) were used to explain the mechanism for the enhanced and hindered photocatalytic performances of the SnO2-modified TiO2 photocatalysts. The results showed that the nanocrystalline cassiterite SnO2 is attached to the TiO2 nanocrystallites through the Sn-O-Ti bonds. In this way, the coupling of two semiconductors, SnO2 and TiO2, was demonstrated. Compared to single-phase photocatalysts, the coupling of semiconductors has a beneficial effect on the separation of charge carriers, which prolongs their lifetime for accessibility to participate in the redox reactions. The maximum increase in activity of the thin films was achieved in the low concentration range (0.1–1 mol.%), which means that an optimal ratio and contact of the two phases is achieved for the given physical parameters such as particle size, shape and specific surface area of the catalyst.
Found in: ključnih besedah
Keywords: photocatalytic activity, Sn-modified TiO2, low-temperature, thin films, XAS analysis
Published: 05.07.2021; Views: 293; Downloads: 0
.pdf Fulltext (5,18 MB)