Growth of MoSe2 thin films and use in electrochemical hydrogen evolution : abstract
Takwa Chouki, Borjana Donkova, Burhan can Aktarla, Plamen Stefanov, Saim Emin, 2020, objavljeni povzetek znanstvenega prispevka na konferenci

Opis: We present the chemical vapor deposition (CVD) approach to grow MoSe2 thin films using colloidal molybdenum nanoparticles (Mo NPs). The synthetic protocol of Mo NPs was achieved using a wet-chemical method. The obtained Mo NPs were spin-coated on graphite substrates and heat-treated in the presence of selenium vapors at several temperatures (≥750 °C). The electrocatalytic activities of heat-treated MoSe2 thin films were studied for hydrogen evolution reaction (HER) in 0.5 M sulfuric acid (H2SO4). The lowest recorded overpotential of 218 mV at 10 mA cm−2 vs. a reversible hydrogen electrode was achieved with MoSe2−800°C catalyst. In addition, electrochemical impedance spectroscopy (EIS) was performed to access the charge-transfer resistance of the MoSe2 films. The colloidal approach combined with CVD is a promising route to produce carbon supported MoSe2 electrocatalyst for HER.
Ključne besede: MoSe2 thin films CVD HER
Objavljeno v RUNG: 06.02.2023; Ogledov: 1158; Prenosov: 0
Gradivo ima več datotek! Več...

2.
Synthesis of efficient iron phosphide catalyst for electrocatalytic hydrogen generation
Takwa Chouki, D. Lazarević, B. Donkova, Saim Emin, 2021, izvirni znanstveni članek

Opis: A solvothermal synthesis of iron phosphide electrocatalysts using triphenylphosphine (TPP) as phosphorus precursor is presented. The synthetic protocol generates Fe2P/FeP phase at 350°C. After deposition of the catalyst onto graphite substrate heat-treatment at higher temperature was carried out. Annealing at 500°C under reductive atmosphere induced structural changes in the Fe2P/FeP samples which yielded a pure Fe2P phase. The electrocatalytic activity of the Fe2P catalyst was studied for hydrogen evolution reaction (HER) in 0.5 M H2SO4. The recorded overpotential for HER was about 130 mV vs. a reversible hydrogen electrode (RHE) at 10 mA cm−2
Ključne besede: solvothermal synthesis, iron phosphide, electrocatalyst, hydrogen evolution
Objavljeno v RUNG: 10.05.2021; Ogledov: 2168; Prenosov: 0
Gradivo ima več datotek! Več...

3.
Growth of MoSe2 electrocatalyst from metallic molybdenum nanoparticles for efficient hydrogen evolution : Growth of MoSe2 electrocatalyst from metallic molybdenum nanoparticles for efficient hydrogen evolution
Takwa Chouki, Boriana Donkova, Burhancan Aktarla, Plamen Stefanov, Saim Emin, 2021, izvirni znanstveni članek

Opis: Molybdenum diselenide (MoSe2) is an emerging alternative to platinum-group-metal electrocatalysts for the hydrogen evolution reaction (HER). Herein, the chemical vapor deposition (CVD) approach was demonstrated to be a successful route to grow MoSe2 thin films using colloidal molybdenum nanoparticles (Mo NPs). T
Ključne besede: Water splitting, electrocatalyst, MoSe2
Objavljeno v RUNG: 15.01.2021; Ogledov: 2410; Prenosov: 0