1.
Efficient Iron Phosphide Catalyst as a Counter Electrode in Dye-Sensitized Solar Cells : article
Abdullah Yildiz, Takwa Chouki, Aycan Atli, Moussab Harb, Sammy W Verbruggen, Rajeshreddy Ninakanti, Saim Emin, 2021, izvirni znanstveni članek

Opis: Developing an efficient material as a counter electrode (CE) with excellent catalytic activity, intrinsic stability, and low cost is essential for the commercial application of dye-sensitized solar cells (DSSCs). Transition metal phosphides have been demonstrated as outstanding multifunctional catalysts in a broad range of energy conversion technologies. Here, we exploited different phases of iron phosphide as CEs in DSSCs with an I–/I3–-based electrolyte. Solvothermal synthesis using a triphenylphosphine precursor as a phosphorus source allows to grow a Fe2P phase at 300 °C and a FeP phase at 350 °C. The obtained iron phosphide catalysts were coated on fluorine-doped tin oxide substrates and heat-treated at 450 °C under an inert gas atmosphere. The solar-to-current conversion efficiency of the solar cells assembled with the Fe2P material reached 3.96 ± 0.06%, which is comparable to the device assembled with a platinum (Pt) CE. DFT calculations support the experimental observations and explain the fundamental origin behind the improved performance of Fe2P compared to FeP. These results indicate that the Fe2P catalyst exhibits excellent performance along with desired stability to be deployed as an efficient Pt-free alternative in DSSCs.
Ključne besede: Iron phosphide, catalyst, counter electrode, dye-sensitized solar cell, solvothermal synthesis
Objavljeno v RUNG: 06.02.2023; Ogledov: 1120; Prenosov: 0
Gradivo ima več datotek! Več...

2.
Highly active iron phosphide catalysts for selective electrochemical nitrate reduction to ammonia
Takwa Chouki, Manel Machreki, Iwona A. Rutkowska, Beata Rytelewska, Pawel Jozef Kulesza, Georgi Tyuliev, Moussab Harb, Luis Miguel Azofra, Saim Emin, 2023, izvirni znanstveni članek

Opis: The electrochemical reduction reaction of the nitrate ion (NO3−), a widespread water pollutant, to valuable ammonia (NH3) is a promising approach for environmental remediation and green energy conservation. The development of high-performance electrocatalysts to selectively reduce NO3− wastes into value-added NH3 will open up a different route of NO3− treatment, and impose both environmental and economic impacts on sustainable NH3 synthesis. Transition metal phosphides represent one of the most promising earth-abundant catalysts with impressive electrocatalytic activities. Herein, we report for the first time the electrocatalytic reduction of NO3− using different phases of iron phosphide. Particularly, FeP and Fe2P phases were successfully demonstrated as efficient catalysts for NH3 generation. Detection of the in-situ formed product was achieved using electrooxidation of NH3 to nitrogen (N2) on a Pt electrode. The Fe2P catalyst exhibits the highest Faradaic efficiency (96 %) for NH3 generation with a yield (0.25 mmol h−1 cm-−2 or 2.10 mg h−1 cm−2) at − 0.55 V vs. reversible hydrogen electrode (RHE). The recycling tests confirmed that Fe2P and FeP catalysts exhibit excellent stability during the NO3− reduction at − 0.37 V vs. RHE. To get relevant information about the reaction mechanisms and the fundamental origins behind the better performance of Fe2P, density functional theory (DFT) calculations were performed. These results indicate that the Fe2P phase exhibits excellent performance to be deployed as an efficient noble metal-free catalyst for NH3 generation.
Ključne besede: iron phosphide, electrocatalysts, nitrates reduction ammonia, DFT calculations
Objavljeno v RUNG: 02.02.2023; Ogledov: 1418; Prenosov: 4