1. Iron phosphide as an efficient electrocatalysts for hydrogen evolution : abstractTakwa Chouki, Manel Machreki, Saim Emin, 2020, objavljeni povzetek znanstvenega prispevka na konferenci Opis: We report the solvothermal synthesis of iron phosphide electrocatalysts using a low-cost phosphorus precursor. The synthetic protocol allows for the preparation of a Fe2P phase at 300°C and FeP phase at 350°C. To enhance the catalytic activities of obtained iron phosphide particles, heat-treatments were carried out at elevated temperatures. Annealing at 500°C induced structural changes in the samples: (i) Fe2P provided a pure Fe3P phase (Fe3P−500°C) and (ii) FeP transformed into a mixture of iron phosphide phases (Fe2P/FeP−500°C). The electrocatalytic activities of heat-treated Fe2P−450°C, Fe3P−500°C, and Fe2P/FeP−500°C catalysts were studied for hydrogen evolution reaction (HER) in 0.5 M sulfuric acid (H2SO4). The lowest recorded overpotential of 110 mV at 10 mA cm−2 vs. a reversible hydrogen electrode was achieved with Fe2P/FeP−500°C catalyst. The present approach allows preparation of immobilized iron phsphide catalyst onto carbon support which is essential for application purpose. The procedure developed by us is an elegant approach to tune the composition of iron phosphide catalyst and control the morphology of particles Ključne besede: solvothermal synthesis
iron phosphide
electrocatalysis
HER Objavljeno v RUNG: 06.02.2023; Ogledov: 2022; Prenosov: 0 Gradivo ima več datotek! Več... |
2. Efficient Iron Phosphide Catalyst as a Counter Electrode in Dye-Sensitized Solar Cells : articleAbdullah Yildiz, Takwa Chouki, Aycan Atli, Moussab Harb, Sammy W Verbruggen, Rajeshreddy Ninakanti, Saim Emin, 2021, izvirni znanstveni članek Opis: Developing an efficient material as a counter electrode (CE) with excellent catalytic activity, intrinsic stability, and low cost is essential for the commercial application of dye-sensitized solar cells (DSSCs). Transition metal phosphides have been demonstrated as outstanding multifunctional catalysts in a broad range of energy conversion technologies. Here, we exploited different phases of iron phosphide as CEs in DSSCs with an I–/I3–-based electrolyte. Solvothermal synthesis using a triphenylphosphine precursor as a phosphorus source allows to grow a Fe2P phase at 300 °C and a FeP phase at 350 °C. The obtained iron phosphide catalysts were coated on fluorine-doped tin oxide substrates and heat-treated at 450 °C under an inert gas atmosphere. The solar-to-current conversion efficiency of the solar cells assembled with the Fe2P material reached 3.96 ± 0.06%, which is comparable to the device assembled with a platinum (Pt) CE. DFT calculations support the experimental observations and explain the fundamental origin behind the improved performance of Fe2P compared to FeP. These results indicate that the Fe2P catalyst exhibits excellent performance along with desired stability to be deployed as an efficient Pt-free alternative in DSSCs. Ključne besede: Iron phosphide, catalyst, counter electrode, dye-sensitized solar cell, solvothermal synthesis Objavljeno v RUNG: 06.02.2023; Ogledov: 1932; Prenosov: 0 Gradivo ima več datotek! Več... |
3. Synthesis and application of transition metal phosphide nanomaterials as electrocatalysts for water splitting and chemical transformations : dissertationTakwa Chouki, 2022, doktorska disertacija Opis: In this thesis, we will focus on the solvothermal synthesis of iron phosphides (FeP, Fe2P) using triphenylphosphine (TPP) as an inexpensive and stable phosphorus source. The obtained iron phosphides were applied as electrocatalysts in hydrogen evolution reaction (HER), oxygen evolution reaction (OER), Rhodamine B (RhB) degradation, Escherichia coli (E. coli) inactivation,
nitrates reduction reaction (NO3RR) to ammonia (NH3), and as counter electrodes in dye-sensitized solar cells (DSSCs). Detailed characterizations of catalysts were carried out to investigate the correlations between the material structure and catalytic activity.
The first part of the thesis gives an introduction to the topic which cover overview of literature about the use of transition metal phosphide as efficient electrocatalysts in water splitting studies, NO3RR to NH3 and DSSCs.
The second part is a description of the experimental methods.
The third part discusses the solvothermal synthesis of FeP and Fe2P catalysts using TPP precursor. The phase conversion of iron phosphides at elevated temperatures under reductive atmosphere was reported. Structural characterizations of the obtained materials were achieved using multiple techniques. The electrocatalytic activities of heat-treated iron phosphide films for HER were studied in acidic environment.
The fourth part discusses the use of Fe2P nanoparticles (NPs) for OER.
The fifth part outlines the use of Fe2P precatalyst in water treatment studies. Using a thin film of Fe2P precatalyst, RhB degradation and E. coli inactivation in the presence of in-situ generated reactive chlorine species were reported. Characterization of Fe2P electrocatalysts before and after the test was carried out using different techniques.
The sixth part shows for the first time the use of FeP and Fe2P as a noble metal-free electrocatalysts for NO3RR to NH3. In this chapter we will emphasize the nitrate reaction pathways, which are highly complex and poorly understood.
The seventh part demonstrates the use of FeP and Fe2P catalysts as robust and efficient counter electrodes in DSSCs. Ključne besede: solvothermal synthesis, iron phosphides, electrocatalysis, HER, OER, RhB degradation, E. coli inactivation, NO3RR to NH3, DSSCs, dissertations Objavljeno v RUNG: 29.08.2022; Ogledov: 3192; Prenosov: 113 Celotno besedilo (6,35 MB) Gradivo ima več datotek! Več... |
4. Solvothermal synthesis of iron phosphides and their application for efficient electrocatalytic hydrogen evolutionTakwa Chouki, Manel Machreki, Saim Emin, 2020, objavljeni povzetek znanstvenega prispevka na konferenci Opis: We report the solvothermal synthesis of iron phosphide electrocatalysts using a low-cost phosphorus precursor [1]. The synthetic protocol allows for the preparation of a Fe2P phase at 300°C and FeP phase at 350°C. To enhance the catalytic activities of obtained iron phosphide particles, heat-treatments were carried out at elevated temperatures. Annealing at 500°C induced structural changes in the samples: (i) Fe2P provided a pure Fe3P phase (Fe3P−500°C) and (ii) FeP transformed into a mixture of iron phosphide phases (Fe2P/FeP−500°C). The electrocatalytic activities of heat-treated Fe2P−450°C, Fe3P−500°C, and Fe2P/FeP−500°C catalysts were studied for hydrogen evolution reaction (HER) in 0.5 M sulfuric acid (H2SO4). The HER activities of the iron phosphide catalyst were found to be phase dependent. The lowest recorded overpotential of 110 mV at 10 mA cm−2 vs. a reversible hydrogen electrode was achieved with Fe2P/FeP−500°C catalyst. The present approach allows the preparation of immobilized iron phsphide catalyst onto carbon support which is essential for application purpose. The procedure developed by us is an elegant approach to tune the composition of iron phosphide catalyst and control the morphology of particles. Ključne besede: solvothermal synthesis, iron phosphide, electrocatalyst, hydrogen evolution, overpotential Objavljeno v RUNG: 13.05.2021; Ogledov: 3471; Prenosov: 0 Gradivo ima več datotek! Več... |
5. |
6. Solvothermal synthesis of iron phosphides and their application for efficient electrocatalytic hydrogen evolutionTakwa Chouki, Manel Machreki, Saim Emin, 2020, izvirni znanstveni članek Opis: Abstract
In this paper, we present a solvothermal synthesis of iron phosphide electrocatalysts using a triphenylphosphine (TPP) precursor. The synthetic protocol generates Fe2P phase at 300 °C and FeP phase at 350 °C. To enhance the catalytic activities of obtained iron phosphide particles heat-treatments were carried out at elevated temperatures. Annealing at 500 °C under reductive atmosphere induced structural changes in the samples: (i) Fe2P provided a pure Fe3P phase (Fe3P−500 °C) and (ii) FeP transformed into a mixture of iron phosphide phases (Fe2P/FeP−500 °C). Pure Fe2P films was prepared under argon atmosphere at 450 °C (Fe2P−450 °C). The electrocatalytic activities of heat-treated Fe2P−450 °C, Fe3P−500 °C, and Fe2P/FeP−500 °C catalysts were studied for hydrogen evolution reaction (HER) in 0.5 M H2SO4. The HER activities of the iron phosphide catalyst were found to be phase dependent. The lowest electrode potential of 110 mV vs. a reversible hydrogen electrode (RHE) at 10 mA cm−2 was achieved with Fe2P/FeP−500 °C catalyst. Ključne besede: Solvothermal synthesis, Iron phosphide, Electrocatalyst, Hydrogen evolution, Overpotential Objavljeno v RUNG: 20.07.2020; Ogledov: 3899; Prenosov: 0 Gradivo ima več datotek! Več... |