Repozitorij Univerze v Novi Gorici

Iskanje po repozitoriju
A+ | A- | Pomoč | SLO | ENG

Iskalni niz: išči po
išči po
išči po
išči po
* po starem in bolonjskem študiju

Opcije:
  Ponastavi


1 - 2 / 2
Na začetekNa prejšnjo stran1Na naslednjo stranNa konec
1.
Elucidation of Donor:Acceptor Phase Separation in Nonfullerene Organic Solar Cells and Its Implications on Device Performance and Charge Carrier Mobility
Sebastian F. Hoefler, Georg Haberfehlner, Thomas Rath, Andreas Keilbach, Mathias Hobisch, Alexander Dixon, Egon Pavlica, Gvido Bratina, Gerald Kothleitner, Ferdinand Hofer, Gregor Trimmel, 2019, izvirni znanstveni članek

Opis: In bulk-heterojunction solar cells, the device performance strongly depends on the donor and acceptor properties, the phase separation in the absorber layer, and the formation of a bicontinuous network. While this phase separation is well explored for polymer:fullerene solar cells, only little is known for polymer:nonfullerene acceptor solar cells. The main hurdle in this regard is often the chemical similarity of the conjugated polymer donor and the organic nonfullerene acceptor (NFA), which makes the analysis of the phase separation via atomic force microscopic (AFM) phase images or conventional transmission electron microscopy difficult. In this work, we use the donor polymer PTB7-Th and the small molecule acceptor O-IDTBR as the model system and visualized the phase separation in PTB7-Th:O-IDTBR bulk-heterojunctions with different donor:acceptor ratios via scanning transmission electron microscopy (STEM) high-angle annular dark-field (HAADF) images and electron energy loss spectroscopy (EELS) based elemental mapping, which resulted in a good contrast between the donor and the acceptor despite very low differences in the chemical composition. AFM as well as grazing-incidence wide-angle X-ray scattering (GIWAXS) investigations support the electron microscopic data. Furthermore, we elucidate the implications of the phase separation on the device performance as well as charge carrier mobilities in the bulk-heterojunction layers, and a high performance of the solar cells was found over a relatively broad range of polymer domain sizes. This can be related to the larger domain sizes of the acceptor phase with higher amounts of O-IDTBR in the blend, while the polymer donor phase still forms continuous pathways to the electrode, which keeps the hole mobility at a relatively constant level.
Ključne besede: nanomorphology bulk-heterojunction scanning transmission electron microscopy organic photovoltaics charge carrier mobility
Objavljeno v RUNG: 15.01.2020; Ogledov: 2919; Prenosov: 85
.pdf Celotno besedilo (6,22 MB)

2.
Amorphous nanocomposite of polycarbosilanes and aluminum oxide
Andraž Mavrič, 2018, doktorska disertacija

Opis: This work presents a paradigm for high temperature stabilization of bulk amorphous aluminium oxide. The thermodynamic stabilization is achieved by preparing a nanocomposite, where polymethylsilane dendritic molecules are dispersed in an aluminium hydroxide gel. Upon heat-treatment the gel transforms to the amorphous aluminium oxide that is stable up to 900°C. The dispersion of the macromolecules and their covalent bonding to the alumina matrix induce homogeneously distributed strain fields that keep the alumina amorphous. The first part of the thesis focuses on the synthesis, characterization and solubility properties of the dendritic polymethylsilane. The polymethylsilane is synthetized by electrochemical polymerization from trichloromethylsilane monomer. The polymerization mechanism, involving a single polymerization pathway, is identified. The polymer growth proceeds through reduction of the monomers to the silyl anions and their addition to the growing polymer. The solubility of three chemically related but topologically different polysilanes (linear, dendritic and network) were studied by dynamic light scattering. At room temperature the agglomerates in a range from 500 to 1300 nm are present. They undergo de-agglomeration at slightly elevated temperatures of around 40°C. The de-agglomeration results in formation of stable solutions, where a hydrodynamic diameter of the individual polymer molecules was measured to be in a range from 20 to 40 nm. The obtained diameters of two dendritic polymethylsilane macromolecules, synthesized under different electrolysis conditions, are much larger than the theoretical size estimated for an ideal dendrimer. We determined by 29Si NMR that the reason for this is in a large number of branching irregularities (defects) contained in the molecular structure. Combining the experimental values obtained by DLS and density measurements with a structural model that considers the branching irregularities, it is shown that the inclusion of the defects allows the dendritic polymer to exceed the sterical limitations and form the hyperbranched dendritic structure. The final size depends on a relative amount of the branching defects. In the second part, the synthetized polymethylsilane molecules were successfully used for the nanocomposite formation. The aluminium hydroxide gel with the dispersed polymethylsilane molecules was prepared as a precursor. Upon heat-treatment it gives the amorphous aluminium oxide stable up to 900°C. The dispersed macromolecules induce homogeneously distributed strain fields that keep the aluminium oxide amorphous during the thermal treatment the dispersed macromolecules covalently bind to the matrix, inducing the interface strain. The amorphous state was confirmed by the presence of penta-coordinated aluminium detected by 27Al NMR and a low bandgap measured by UV-vis absorption spectroscopy.
Ključne besede: amorphous aluminium oxide, polymethylsilane, nanocomposite, electropolymerization, solubility, agglomeration, de-agglomeration, dendrimer, hyperbranched dendritic structure, dynamic light scattering, thermal analysis, transmission electron microscopy, scanning electron microscopy, X-ray diffraction, infrared spectroscopy, UV-Vis spectroscopy
Objavljeno v RUNG: 19.07.2018; Ogledov: 6009; Prenosov: 210