Naslov:In-situ XAS analysis of nanoshaped CuO/CeO2 catalysts used for N2O decomposition
Avtorji:ID Arčon, Iztok, UNG (Avtor)
ID Zabilsky, Maxim, Kemijski inštitut Ljubljana (Avtor)
ID Djinović, Petar, Kemijski inštitut Ljubljana (Avtor)
ID Pintar, Albin, Kemijski inštitut Ljubljana (Avtor)
Datoteke: Gradivo nima datotek, ki so prostodostopne za javnost. Gradivo je morda fizično dosegljivo v knjižnici fakultete, zalogo lahko preverite v COBISS-u. Povezava se odpre v novem oknu
Jezik:Angleški jezik
Vrsta gradiva:Delo ni kategorizirano
Tipologija:1.12 - Objavljeni povzetek znanstvenega prispevka na konferenci
Organizacija:UNG - Univerza v Novi Gorici
Opis:The goal of this research is to establish the working state and correlations between atomic structure and catalytic activity of nanoshaped CuO/CeO2 catalysts used in N2O decomposition reaction. The catalysts contained CuO nanoclusters dispersed over different CeO2 morphologies: nano-rods and nano-cubes. N2O is a side product of nitric and adipic acid production and a very potent greenhouse gas that is formed in amounts estimated at about 400 Mt/a of CO2 equivalent. Consequently, the development of robust, active and selective catalysts for N2O decomposition is of a great environmental and economical interest. CeO2-based materials promoted by CuO represent a new class of catalysts that exhibit considerable activity in N2O decomposition reaction between 300 and 500 °C [1-3], and are significantly cheaper and more efficient than Pt, Pd or Rh based catalysts. In order to maximize the efficiency of the catalyst, the active site in this reaction needs to be identified and the mechanism clarified. In-situ Cu K-edge and Ce L3-edge XANES and EXAFS analysis was done on a set of CuO/CeO2 catalysts with different ceria morphology (nano-cubes, nano-rods) and Cu loadings between 2 to 8 wt. %, during N2O decomposition reaction, under controlled reaction conditions at 400 °C. The XAS spectra were measured in-situ, in a tubular reactor, filled with protective He atmosphere at 1 bar, first at RT, then during heating, and at final temperature of 400 °C, during catalytic reaction, when the catalyst was exposed to a small amount (0.2 vol%) of N2O mixed with He. The Cu K-edge and Ce L3-edge XANES and EXAFS analysis reveals changes in valence and local structure of Cu and Ce in the CuO/CeO2 catalysts. In the initial state (in He at RT), copper is present in the form of CuO nanoparticles attached to the CeO2 surface. After heating in He to 400 °C, partial (10%) reduction of Ce [Ce(IV)→Ce(III)] is detected, significant part of Cu(II) is reduced to Cu(I) and Cu(0) species, and direct Cu-Cu bonds are formed. During catalytic N2O decomposition at 400°C, all Ce(III) is oxidized back to Ce(VI), and a major part of Cu is oxidized back to Cu(II), with about 5% of Cu(I) remaining in equilibrium state. Observed structural and valence changes of copper strongly depend on its loading and CeO2 morphology. With systematic In-situ XAS analysis of different nanoshaped CuO/CeO2 catalysts, we identified the structural characteristics and changes of Cu and Ce phases during catalytic N2O decomposition reaction, which could lead to identification of the active catalytic site during the reaction and further improve the performance of these promising catalytic materials.
Ključne besede:EXAFS, CuO/CeO2 catalyst, N2O decomposition
Leto izida:2018
Št. strani:2
PID:20.500.12556/RUNG-4078-33caf7d2-c262-9ed4-b05d-e5f429618d89 Novo okno
COBISS.SI-ID:5220859 Novo okno
Datum objave v RUNG:12.09.2018
Število ogledov:3846
Število prenosov:0
Kopiraj citat
Skupna ocena:(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
Objavi na:Bookmark and Share

Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše podrobnosti ali sproži prenos.

Gradivo je del monografije

Naslov:Book of abstract, 17 International Conference on X-Ray Absorption Fine Structure, XAFS 2018
Uredniki:Damian Paliwoda
Kraj izida:Krakow
Založnik:Polish Synchrotron Radiation Society
Leto izida:2018
Prireditelj konference:Polish Synchrotron Radiation Society