Naslov:Characterization of bacterial cellulose films combined with chitosan and polyvinyl alcohol: Evaluation of mechanical and barrier properties
Avtorji:ID Cazón, Patricia (Avtor)
ID Velazquez, Gonzalo (Avtor)
ID Vazquez, Manuel (Avtor)
Datoteke: Gradivo nima datotek, ki so prostodostopne za javnost. Gradivo je morda fizično dosegljivo v knjižnici fakultete, zalogo lahko preverite v COBISS-u. Povezava se odpre v novem oknu
Jezik:Angleški jezik
Vrsta gradiva:Delo ni kategorizirano
Tipologija:1.01 - Izvirni znanstveni članek
Organizacija:UNG - Univerza v Novi Gorici
Opis:Bacterial cellulose (BC) produced by Komagataeibacter xylinus is a biomaterial with a unique three-dimensional structure. To improve the mechanical properties and reinforce the BC films, they were immersed in polyvinyl alcohol (0–4%) and chitosan (0–1%) baths. Moisture content, mechanical properties and water vapour perme- ability were measured to assess the effect of polyvinyl alcohol and chitosan. The morphology, optical, structural and thermal properties were evaluated by scanning electron microscopy, spectral analysis, thermogravimetry and differential scanning calorimetry. Results showed that moisture content was significantly affected by the chitosan presence. Tensile strength values in the 20.76–41.65 MPa range were similar to those of synthetic polymer films. Percentage of elongation ranged from 2.28 to 21.82% and Young's modulus ranged from 1043.88 to 2247.82 MPa. The water vapour permeability (1.47×10−11–3.40×10−11 g/m s Pa) decreased with the addition of polyvinyl alcohol. The developed films own UV light barrier properties and optimal visual appearance.
Ključne besede:Films, Bacterial cellulose, Water vapor permeability, Chitosan, Polyvinyl alcohol, UV protection
Leto izida:2019
Št. strani:72-85
Številčenje:1, 216
PID:20.500.12556/RUNG-6026 Novo okno
COBISS.SI-ID:42581507 Novo okno
DOI:10.1016/J.CARBPOL.2019.03.093 Novo okno
NUK URN:URN:SI:UNG:REP:16KTMHHX
Datum objave v RUNG:14.12.2020
Število ogledov:2221
Število prenosov:0
Metapodatki:XML RDF-CHPDL DC-XML DC-RDF
:
Kopiraj citat
  
Skupna ocena:(0 glasov)
Vaša ocena:Ocenjevanje je dovoljeno samo prijavljenim uporabnikom.
Objavi na:Bookmark and Share


Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše podrobnosti ali sproži prenos.

Gradivo je del revije

Naslov:Carbohydrate Polymers
Leto izida:2019

Licence

Licenca:CC BY-NC-ND 4.0, Creative Commons Priznanje avtorstva-Nekomercialno-Brez predelav 4.0 Mednarodna
Povezava:http://creativecommons.org/licenses/by-nc-nd/4.0/deed.sl
Opis:Najbolj omejujoča licenca Creative Commons. Uporabniki lahko prenesejo in delijo delo v nekomercialne namene in ga ne smejo uporabiti za nobene druge namene.
Začetek licenciranja:14.12.2020

Nazaj