| Naslov: | Structural and chemical analysis of hard carbon negative electrode for Na-ion battery with X-ray Raman scattering and solid-state NMR spectroscopy |
|---|
| Avtorji: | ID Rajh, Ava, IJS (Avtor)
ID Gabrijelčič, Matej, KI (Avtor)
ID Tratnik, Blaž, KI (Avtor)
ID Bučar, Klemen, IJS (Avtor)
ID Arčon, Iztok, UNG (Avtor)
ID Petric, Marko, IJS (Avtor)
ID Dominko, Robert, KI (Avtor)
ID Vižintin, Alen, KI (Avtor)
ID Kavčič, Matjaž, IJS (Avtor) |
|---|
| Datoteke: |  Na-ion.pdf (7,76 MB)
MD5: 69D37977EF24BA0E6721D715585A31A4
1-s2.0-S0008622324006171-main.pdf (2,78 MB)
MD5: 58ECB941A2C27194E8D259B87BC285DA
 https://www.sciencedirect.com/science/article/pii/S0008622324006171?via%3Dihub
|
|---|
| Jezik: | Angleški jezik |
|---|
| Vrsta gradiva: | Delo ni kategorizirano |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: | UNG - Univerza v Novi Gorici
|
|---|
| Opis: | This study explores the structural changes of hard carbon (HC) negative electrodes in sodium-ion batteries induced by insertion of Na ions during sodiation. X-ray Raman spectroscopy (XRS) was used to record both C and Na K-edge absorption spectra from bulk HC anodes carbonized at different temperatures and at several points during sodiation and desodiation. Comparing the [pi]*/[sigma]*
regions in the C K-edge spectra sp2/sp3 hybridization ratio of material was determined. Higher carbonization temperatures led to increased order in graphitic structure and shorter bond lengths. Sodiation caused a decrease in graphitic layer order due to inserted Na ions. Complementary operando solid state 23Na nuclear magnetic resonance (ssNMR) studies confirmed the structural changes, while showing pore filling mechanism, which is not observed in ex situ measurements, primarily at higher carbonization temperatures. XRS analysis of Na K-edge spectra revealed systematic variations in the solid electrolyte interface (SEI) composition during cycling. Changes in XRS spectra were attributed to both SEI composition alterations, accompanied by the insertion/adsorption of Na ions at defect sites within the carbon structure. |
|---|
| Ključne besede: | hard carbon, RIXS, carbon XANES, EXAFS, NMR, Na battery |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Datum objave: | 01.09.2024 |
|---|
| Št. strani: | str. 1-14 |
|---|
| Številčenje: | 2024, Vol. 228, [article no.] 119398 |
|---|
| PID: | 20.500.12556/RUNG-9189  |
|---|
| COBISS.SI-ID: | 201116419 |
|---|
| UDK: | 544.5/.6 |
|---|
| ISSN pri članku: | 1873-3891 |
|---|
| DOI: | 10.1016/j.carbon.2024.119398 |
|---|
| NUK URN: | URN:SI:UNG:REP:6WPFWJBD |
|---|
| Datum objave v RUNG: | 10.09.2024 |
|---|
| Število ogledov: | 272 |
|---|
| Število prenosov: | 0 |
|---|
| Metapodatki: |     |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Skupna ocena: | (0 glasov) |
|---|
| Vaša ocena: | Ocenjevanje je dovoljeno samo prijavljenim uporabnikom. |
|---|
| Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |